並列タイトル等Study on Pb-Bi Corrosion of Structural and Fuel Cladding Materials for Nuclear Applications,3; Corrosion investigation of steels between 500 and 650circC during 10,000 h of exposure to stagnant liquid Pb-Bi containing 10-6 wt% of oxygen
一般注記This is the third report on the compatibility of structural and fuel cladding materials that has to be investigated for a possible advanced heavy metal cooled reactor system. The first two reports considered the behavior of 316 FR, P122 and ODS steels during 800, 2,000 and 5,000 h in stagnant LBE at 500 - 650$^{\circ}$C containing 10-6 wt\% of oxygen. This report describes the results of all experiments including that of 10,000 h duration. Martensitic steels perform well at 500 and 550$^{\circ}$C up to the maximal exposure time of 10,000 h, while austenites fail after 5,000 h. At temperatures of 600$^{\circ}$C and 650$^{\circ}$C all of the steels fail the earlier the higher the temperature is. Steels with Al - alloying at the surface by the GESA process withstand corrosion up to the maximal exposure time at all of the applied temperatures if it is ensured that the Al - concentration at the surface is in between 8 - 15 wt\%.
本報告書は、重金属冷却炉への適用が検討されている炉心・構造材料の鉛ビスマス中における耐食性評価に関する第3報である。第1報および第2報では、10-6wt\%の酸素を含有する500$^{\circ}$Cから650$^{\circ}$Cの停留鉛ビスマス中における316FR、P122(12Cr鋼)およびODS-M鋼の800、2,000および5,000時間浸漬後の腐食挙動について報告した。本報告書では、これらの試験結果を含め、10,000時間までのこれら3鋼種の腐食挙動について報告する。500$^{\circ}$Cおよび550$^{\circ}$Cの鉛ビスマス中では、マルテンサイト鋼であるP122およびODSの受入材は10,000時間までの浸漬に対して、表面に形成された酸化(保護)皮膜による良好な耐食性を示した。一方、オーステナイト鋼である316FR受入材は5,000時間浸漬後にはその効果が認められなくなった。600$^{\circ}$Cおよび650$^{\circ}$Cでは全ての鋼種で酸化皮膜による保護効果が認められなかった。これら3鋼種のアルミニウム表面改質材(GESA材)については、表面のアルミニウム濃度が8$\sim$15wt\%に保たれた場合は、全ての試験ケースで耐食性は良好であった。
一次資料へのリンクURL/JNC-TY9400-2003-026.pdf （fulltext）
連携機関・データベース国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）
提供元機関・データベース日本原子力研究開発機構 : JOPSS:JAEA Originated Papers Searching System