並列タイトル等Continuous Monitoring of Back-Wall Stress Corrosion Cracking Propagation by Means of Potential Drop Techniques
一般注記In order to investigate the applicability of the potential drop techniques to the continuous monitoring of stress corrosion cracking (SCC) propagation, SCC tests were performed in a sodium thiosulfate solution at room temperature using plate specimens with weldments. The SCC propagation was monitored using the techniques of direct current potential drop (DCPD), alternating current potential drop (ACPD) and modified induced current potential drop (MICPD) on the reverse side that on which the SCC existed and effectiveness of each technique for the continuous monitoring from the reverse side of SCC was compared from the viewpoints of sensitivity to the crack propagation and measurement stability. The MICPD and DCPD techniques permit continuous monitoring of the backwall SCC propagation, which initiates from a fatigue pre-crack at a depth of about 4mm, from which it propagates through more than 80% of the specimen thickness. The MICPD technique can decrease the effect of the current flowing in the direction of the crack length by focusing the induced current into the local area of measurement using induction coils, so that the sensitivity of the continuous monitoring of the back wall SCC propagation is higher than that of the DCPD and ACPD techniques.
一次資料へのリンクURLhttps://u-fukui.repo.nii.ac.jp/?action=repository_action_common_download&item_id=22275&item_no=1&attribute_id=22&file_no=1
連携機関・データベース国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）