タイトル(掲載誌)Journal of Nuclear Materials
一般注記Vanadium alloys, including the highly purified V-4Cr-4Ti alloy called NIFS-Heat2, in the form of sodium-enclosed irradiation capsules, were irradiated up to a damage level of 5dpa in the Joyo reactor at temperatures from 395 to 601°C. An increase of the ductile–brittle transition temperature (DBTT) by neutron irradiation and irradiation hardening were observed. No significant loss of ductility was observed even for irradiation at 395 and 450°C. The addition of titanium to V-Cr alloys was effective for irradiation hardening at high temperature. Hydrogen uptake in the cleaning process during dismantling of the irradiation capsules caused ductility loss of the highly purified V-4Cr-4Ti alloys; the alloys recovered their ductility when they were annealed at 400°C in vacuum. The uniform formation of Ti(OCN) precipitate was suppressed in highly purified V-4Cr-4Ti alloys irradiated in Joyo in a liquid-sodium environment.
一次資料へのリンクURLhttps://u-fukui.repo.nii.ac.jp/?action=repository_action_common_download&item_id=22293&item_no=1&attribute_id=22&file_no=1
関連情報(DOI)10.1016/j.jnucmat.2008.12.185
連携機関・データベース国立情報学研究所 : 学術機関リポジトリデータベース(IRDB)(機関リポジトリ)