Fracture strength of telescopic zirconia secondary crowns of different taper and thickness

• 資料種別: 博士論文
• タイトル: Fracture strength of telescopic zirconia secondary crowns of different taper and thickness
• 著者・編者: 柴田, 駿亮
• 著者標目: 柴田, 駿亮
• 並列タイトル等: テーパー角および厚さの異なるジルコニアを用いたテレスコープクラウンの外冠の破折強度
• 授与機関名: 大阪歯科大学
• 授与年月日: 2021-03-05
• 報告番号: 甲第910号
• 学位: 博士（歯学）
• 本文の言語コード: eng
• 件名標目: Telescopic crowns｜Y-TZP｜ Zirconia｜ Fracture strength
• 対象利用者: 一般
• 一般注記: The objective of this study was to clarify the influence of the half taper angle and thickness of the zirconia secondary crown on its fracture strength. Y-TZP was used for both primary and secondary crown. Samples were prepared at the half taper angles of 2° and 4° and a secondary crown thickness of 0.5 and 1.0 mm (n=7). The secondary crown was restored on the primary crown and the fracture strength was determined by loading all specimens until fracture using a universal testing machine. The load applied at the time of secondary crown fracture was regarded as fracture strength. Based on the analysis of variance, although the fracture strength at 1.0-mm thickness was significantly greater than that at 0.5-mm thickness, the taper angle had no influence on the fracture strength.; 2020年度
• オンライン閲覧公開範囲: インターネット公開
• 著作権情報: CC BY-NC-ND
• 連携機関・データベース: 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• 提供元機関・データベース: 大阪歯科大学 : 大阪歯科大学学術リポジトリ

目次

https://osaka-dent.repo.nii.ac.jp/?action=repository_action_common_download&item_id=297&item_no=1&attribute_id=20&file_no=2 fulltext

https://osaka-dent.repo.nii.ac.jp/?action=repository_action_common_download&item_id=297&item_no=1&attribute_id=20&file_no=1 fulltext