Wear Properties of Rapidly Solidified P/M Aluminum Alloys with High Strength
タイトル(掲載誌)総合技術研究所研究報告=Bulletin of Research Institute for Industrial Technology.
一般注記High- strength P/M (powder metallurgy) aluminum alloys of Al-Ni-Y-Co, Al-Si-Ni-Ce and Al-Ti-Fe-TM(TM : Cr, Mo, V, Zr) systems were prepared by extrusion of rapidly solidified powders which were produced by high-pressure He gas atomization. It was found that wear resistance of the P/M aluminum alloys thus prepared was better than that of the conventional aluminum alloys. Al_<89>(Ni_<0.33>Y_<0.54>Co_<0.13>)_<11> alloy had the best wear resistance among the P/M aluminum alloys studied in this experiment. In order to investigate the cause of the difference of wear properties in those P/M aluminum alloys, wear traces and wear particles were analyzed by EPMA, SEM, TEM and Micro-Vickers hardness measurement. It was found that the hard oxide layer was formed on the surface of the wear trace in Al_<89>(Ni_<0.33>Y_<0.54>Co_<0.13>)_<11> alloy. However, in the case of Al_<78.5>Si_<19>Ni_2Ce_<0.5> alloy, wear particles were included in the surface of the wear trace. It is considered that the oxidation of wear surface and the stability of the formed oxide layer significantly influenced wear resistance of the P/M aluminum alloy.
identifier:http://repository.aitech.ac.jp/dspace/handle/11133/1576
一次資料へのリンクURLhttp://repository.aitech.ac.jp/dspace/bitstream/11133/1576/1/%e7%b7%8f%e7%a0%941%e5%8f%b7%28P91-96%29.pdf
連携機関・データベース国立情報学研究所 : 学術機関リポジトリデータベース(IRDB)(機関リポジトリ)