並列タイトル等ZrC リュウシ オ フクム Zr_55Al_10Ni_5Cu_30 バルク キンゾク ガラス フクゴウ ザイリョウ ノ ナノ ケッショウカ キョドウ
Nanocrystallization of Zr_55Al_10Ni_5Cu_30 Bulk Metallic Glass Conposites Containing ZrC Particles
タイトル(掲載誌)総合技術研究所研究報告=Bulletin of Research Institute for Industrial Technology.
一般注記Zr_55Al_10Ni_5Cu_30 bulk metallic glass composite containing 10 vol% crystalline ZrC particles was prepared by an in-situ reaction between Zr-based melt and graphite powder being followed by an injection casting into a copper mould. The crystallization process of the composites during annealing at 723K has been investigated by using DSC, X-ray diffraction, TEM and hardness test. It is found that an unknown crystalline phase appears at first along the interface between ZrC particle and the matrix of the composite, and then a homogeneous nanocrystallization occurs in the matrix. The nanocrystalline phase precipitated in the matrix has a higher hardness than the hardness of the amorphous phase which remained in the matrix. Hardness of the matrix increases with increasing the volume fraction of the nanocrystalline phases. After annealed at 723K for 40min, most of the matrix has been transformed into crystalline phases with a final average grain size of about 120nm.
identifier:http://repository.aitech.ac.jp/dspace/handle/11133/1594
一次資料へのリンクURLhttp://repository.aitech.ac.jp/dspace/bitstream/11133/1594/1/%e7%b7%8f%e7%a0%943%e5%8f%b7%28P45-49%29.pdf
連携機関・データベース国立情報学研究所 : 学術機関リポジトリデータベース(IRDB)(機関リポジトリ)