並列タイトル等CPCモンモリロナイトを含む新規歯科用レジンセメントに関する検討
一般注記Objective: The aim of this study was to evaluate the mechanical property, bonding performance and anti-microbial activity of a novel resin cement containing montmorillonite modified Cetylpyridinium chloride (CPC-Mont), and to determine the optimal particle size and concentration of CPC-Mont to be lorded to the resin cement. Materials and methods: Montmorillonite filler modified CPC with a median diameter of 30μm and 7μm were prepared, and they lorded to a resin cement at concentrations of 2, 3, 4, 5, 7.5 wt.%. Mechanical property and bonding performance of the resin cements were evaluated by 3 point bending test and micro-tensile bond strength test. The amount of CPC released from the resin disks were quantified using a UV-vis recording spectrophotometer. The anti-biofilm activity was also studied using scanning electron microscope. Results: Mechanical property and bonding performance of the resin cement decreased with lording 30μm CPC-Mont, but no reduction was observed with lording 7μm CPC-Mont. Although CPC release was decreased as the immersion period passed, 5 and 7.5 wt.% CPC-Mont resin cement inhibited biofilm formation for 30 days. Conclusions: The lording of CPC-Mont with a median diameter of 7μm at concentrations of 5 to 7.5 wt.% to resin cement was effective in achieving continuous anti-biofilm activity while maintaining the mechanical property and bonding performance.
(主査) 教授 吉田 靖弘, 教授 井上 哲, 教授 佐野 英彦
歯学院(口腔医学専攻)
コレクション(個別)国立国会図書館デジタルコレクション > デジタル化資料 > 博士論文
受理日(W3CDTF)2021-06-07T02:06:26+09:00
連携機関・データベース国立国会図書館 : 国立国会図書館デジタルコレクション