並列タイトル等強度と注入性に優れるβ-TCP基セメントへのジルコニア添加の効果
一般注記Injectable calcium phosphate cements (CPCs) exhibit many advantages as bone substitution materials. However, the strength of injectable CPCs after setting are often insufficient. In our previous studies, mechano-chemically modification of β-tricalcium phosphate cement powder through a planetary ball-milling process exhibited simultaneous improvement in the strength and injectability of CPC. Two plausible effects of this process are: changes in the CPC powder properties and zirconia abrasion powder contamination from the milling pot and balls. The objective of the present study is to separately evaluate these two effects on the strength and injectability of CPCs.The calculated injectability of the cement paste with and without the addition of zirconia powder were higher than 65% at 6 h after mixing. These values were much higher than that of the CPC paste without mechano-chemically modification, and similar to that of CPC with zirconia abrasion powder contamination. By contrast, the compression strength of the set CPC with zirconia powder additives were higher than that without the addition, and similar to that of CPC with zirconia abrasion powder contamination. These results suggest that the changes in the CPC powder properties due to mechano-chemically modification mainly affected the injectability of the CPC paste, and the zirconia abrasion powder contamination of the CPC powder affected the strength of the set CPC.
DOIinfo:doi/10.1016/j.ceramint.2020.09.017
コレクション（個別）国立国会図書館デジタルコレクション > デジタル化資料 > 博士論文
受理日（W3CDTF）2021-07-05T22:24:43+09:00
連携機関・データベース国立国会図書館 : 国立国会図書館デジタルコレクション