A Failure Criterion to Explain the Test Specimen Thickness Effect on Fracture Toughness in the Transition Temperature Region

Material type: 文書・図像類

Author: Meshii, Toshiyukiほか

Publisher: -

Publication date: 2013-05

Material Format: Digital

Capacity, size, etc.: -

NDC: -

View All

Notes on use

Note (General)：: This paper considered the test specimen thickness (TST) effect on the fracture toughness of a material Jc in the transition temperature region for 3 p...

Search by Bookstore

Holdings of Libraries in Japan

This page shows libraries in Japan other than the National Diet Library that hold the material.

List of Cooperating Institutions and Databases

Please contact your local library for information on how to use materials or whether it is possible to request materials from the holding libraries.

other

Ｕｎｉｖｅｒｓｉｔｙ　ｏｆ　Ｆｕｋｕｉ　Ａｃａｄｅｍｉｃ　Ｒｅｐｏｓｉｔｏｒｙ
Digital
You can check the holdings of institutions and databases with which Institutional Repositories DataBase(IRDB)(Institutional Repository) is linked at the site of Institutional Repositories DataBase(IRDB)(Institutional Repository).
Ｕｎｉｖｅｒｓｉｔｙ　ｏｆ　Ｆｕｋｕｉ　Ａｃａｄｅｍｉｃ　Ｒｅｐｏｓｉｔｏｒｙ

Search by Bookstore

Bibliographic Record

You can check the details of this material, its authority (keywords that refer to materials on the same subject, author's name, etc.), etc.

Digital

Material Type: 文書・図像類
Title: A Failure Criterion to Explain the Test Specimen Thickness Effect on Fracture Toughness in the Transition Temperature Region
Author/Editor: Meshii, Toshiyuki
Lu, Kai
Takamura, Ryota
Author Heading: Meshii, Toshiyuki
Lu, Kai
Takamura, Ryota
Publication Date: 2013-05
Publication Date (W3CDTF): 2013-05
Periodical title: Engineering Fracture Mechanics
No. or year of volume/issue: 104
Volume: 104
Pages: 184-197
ISSN (Periodical Title): ISSN : 0013-7944
Text Language Code: eng
Subject Heading: Fracture mechanics
Constraint effect
Fracture toughness
Cleavage fracture
Transition temperature
Thickness effect
3PB specimen
Target Audience: 一般
Note (General): This paper considered the test specimen thickness (TST) effect on the fracture toughness of a material Jc in the transition temperature region for 3 point bending (3 PB) specimens. Fracture toughness tests and elastic-plastic finite element analyses (FEA) with non-standard test specimens, which are non-standard because the specimen thickness-to-width ratio B/W was varied in the range of 0.25 to 1.5, were conducted. Based on these tests and the FEA results, it was demonstrated that the “planar" (4δt, σ22c) failure criterion-which states that cleavage fracture after significant plastic deformation occurs when the crack opening stress σ22 at a distance from the crack-tip that is equal to 4 times the crack-tip opening displacement δt exceeds a critical value σ22c-was verified to effectively explain the TST effect. This (4δt, σ22c) criterion also successfully predicted the tendency of Jc to saturate to some bounding value for B/W = 1.0. This tendency was similar to that of the T33-stress, which is the out-of-plane elastic crack-tip constraint parameter. Because the (4δt, σ22c) criterion could predict the TST effect on Jc and because the criterion could predict the bounded behavior of Jc for large B/W, the TST effect was concluded to be mainly mechanical in nature, which the weakest link model fails to predict. The mechanical cause of the TST effect on Jc was considered to be an out-of-plane crack-tip constraint, and one of its measures of magnitude is the T33-stress.
Access Restrictions: 限定公開
Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）
https://irdb.nii.ac.jp
Original Data Provider (Database): 福井大学 : 福井大学学術機関リポジトリ