Approaches to the thermally stable poly(lactide)s with stereocomplex as a unique crystalline component

• Material Type: 博士論文
• Title: Approaches to the thermally stable poly(lactide)s with stereocomplex as a unique crystalline component
• Author/Editor: ESRAA MOHAMED ELMOATASEM IBRAHIM ELKHODARY
• Author Heading: ESRAA MOHAMED ELMOATASEM IBRAHIM ELKHODARY
• Publication Date: 2017-09-25
• Publication Date (W3CDTF): 2017-09-25
• Alternative Title: ポリ乳酸ステレオコンプレックス形成に及ぼす成分ポリマーの分子量と混合条件の影響および耐熱性ポリ乳酸二軸延伸フィルムの構造物性
• Degree grantor/type: 京都工芸繊維大学
• Date Granted: 2017-09-25
• Dissertation Number: 甲第858号
• Degree Type: 博士（工学）
• Text Language Code: eng
• Subject Heading: PLLA; PDLA; PLLA/PDLA blend; melt blending; cast film; crystallinity; stereocomplex; stereocomplex crystallization; homocrystal; Tg; Tc; synthesis; polymerization
• Target Audience: 一般
• Note (General): type:Thesis; Thesis Abstract (In approx. 300 English words) Blends of poly(L-lactic acid) (PLLA) and poly(D-lactic acid) (PDLA) forms stereocomplex crystal (sc) which shows a melting point around 230oC, about 50oC higher than that of PLLA and PDLA homo crystal (hc). The degree of sc is affected by the method and condition of mixing, the optical purity and the molecular weight of parent poly(lactide)s, and by the mixing ratio. Among these factors, the effects of the molecular weight of parent polymers and the mixing condition on the stereocomplexation of the equal bends of PLLA and PDLA are determined in this study. Further the effect of the processing condition on the physical property and the higher-order structure of the biaxially oriented PLLA/PDLA blend films were studied. The effect of the molecular weight on the hc crystallization of PLLAs is those known for various semi-crystalline polymers. However there are both lower and higher threshold of the molecular weight exist for sc crystallization. Lower threshold of the molecular weight for the sc crystallization of PLLA/PDLA blend is about 1,000, while that for hc crystallization of PLLA is about 2,500. When the molecular weight is higher than 25,000, both hc and sc tended to form in the blend. The effect of the mixing condition on the sc formation of the PLLA/PDLA blends was investigated. The blends melt-mixed at 200oC and 210oC under application of a high shear flow tend to show a single melting peak of the sc. Further kneading of the blends at an elevated temperature caused the transesterification between the same enatiomeric chains forming block copolymers of L- and D-chains. This block copolymer acts as a nucleating agent of sc and the compatibilizing agent between PLLA and PDLA and promotes the formation of SC. PLLA/PDLA blend was prepared at an optimum condition. The blend was compression molded into films and biaxially drawn and annealed. The biaxially drawn films showed a broad crystalline WAXD reflection and the application of annealing completely changed the reflections into those of sc. The mechanical property was improved by the biaxial drawing and the annealing for short period of time.
• Format (IMT): application/pdf
• Source: fulltext; http://repository.lib.kit.ac.jp/repo/repository/10212/2434/D1-0858_h1.pdf; http://repository.lib.kit.ac.jp/repo/repository/10212/2434/D1-0858.pdf; http://repository.lib.kit.ac.jp/repo/repository/10212/2434/D1-0858_y1.pdf
• Access Restrictions: インターネット公開
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 京都工芸繊維大学 : ＫＩＴ学術成果コレクション