CHANICAL PROPERTIES AND INITIAL FRACTURE BEHAVIOR OF WOVEN FABRIC REINFORCED COMPOSITES

• Material Type: 博士論文
• Title: CHANICAL PROPERTIES AND INITIAL FRACTURE BEHAVIOR OF WOVEN FABRIC REINFORCED COMPOSITES
• Author/Editor: XU, ZHILAN
• Author Heading: XU, ZHILAN
• Publication Date: 2018-09-25
• Publication Date (W3CDTF): 2018-09-25
• Alternative Title: 織物強化複合材料の力学特性及び初期破壊挙動に関する研究
• Degree grantor/type: 京都工芸繊維大学
• Date Granted: 2018-09-25
• Dissertation Number: 甲第903号
• Degree Type: 博士（工学）
• Text Language Code: eng
• Subject Heading: Woven fabric reinforced composites; Initial fracture; Numerical simulation
• Target Audience: 一般
• Note (General): type:Thesis; This research is conducted on the mechanical properties and initial fracture behavior of woven fabric reinforced composites. Several kinds of woven fabrics in different structures, such as plain woven fabric, twill woven fabric, multi-axial knit fabric, were used as reinforcement in this study. In chapter 2, glass woven cloth reinforced composite was fabricated by hand lay-up molding method. Tensile test was carried out on specimens cut in 6 degrees. After that the tensile property was discussed and a basic FEM model was built according to the geometric parameters. On the basis of this work, several effecting factors of interface were put forward and the following researches were conducted. In chapter 3, a typical thermoplastic resin, polyamide 6 (PA6) was used as matrix and carbon twill cloth as reinforcement to fabricate CF/PA6 by hot compression molding. Their failure behaviors and mechanical properties were investigated. In chapter 4, investigation on the initial fracture behavior was carried out on two kinds of roving glass woven fabric reinforced composites manufactured by the hand lay-up method. Two kinds of roving glass woven fabrics of different FAW (Fabric Area Weight) were adopted in this study. A model, of which the intersection part was improved was built on the consideration of the observation results. By combining the experimental results and simulation analyses, the initial behavior of fracture progression in glass-carbon hybrid composite materials are discussed and predicted. In chapter 5, carbon/glass intra-hybrid woven fabric as reinforcement and vinyl ester resin as matrix, CF/GF composite was manufactured through hand lay-up method. Then, the investigation on the mechanical property and initial fracture behavior was carried out. Initial fracture stress was the main factor of initial damage which discussed with AE characteristics during mechanical test. Simulation by software Marc was carried out to analyze the initial fracture behavior. In chapter 6, multi-axial warp knitted fabrics were adopted as reinforcement and the initial fracture behavior was investigated and analyzed. At last, a summary of the whole thesis was presented in Chapter 7.
• Format (IMT): application/pdf
• Source: fulltext; http://repository.lib.kit.ac.jp/repo/repository/10212/2500/D1-0903_h1.pdf; http://repository.lib.kit.ac.jp/repo/repository/10212/2500/D1-0903.pdf
• Access Restrictions: インターネット公開
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 京都工芸繊維大学 : ＫＩＴ学術成果コレクション