交流インピーダンス法によるコンクリートの鉄筋腐食の新しい検査法の開発

• Material Type: 文書・図像類
• Title: 交流インピーダンス法によるコンクリートの鉄筋腐食の新しい検査法の開発
• Author/Editor: 鳥居, 和之; Torii, Kazuyuki
• Author Heading: 鳥居, 和之; Torii, Kazuyuki
• Publication, Distribution, etc.: 金沢大学工学部
• Publication Date: 1997-03
• Publication Date (W3CDTF): 1997-03
• Alternative Title: Development of New Method for Corrosion of Steel Reinforcement in Concrete Using AC Impedance
• Periodical title: 平成8(1996)年度 科学研究費補助金 基盤研究(C) 研究成果報告書 = 1996 Fiscal Year Final Research Report
• No. or year of volume/issue: 1995-1996
• Volume: 1995-1996
• Pages: 5p.-
• Text Language Code: jpn
• Subject Heading: 交流インピーダンス法; 急速試験法(AASHTO T277); 比抵抗; 鉄筋腐食; 塩化物イオン拡散係数; 鉱物質混和材; 高炉スラグ微粉末コンクリート; AC Impedance Method; Rapid Chloride Permeability Test (AASHTO T277); Electrical Resistivity; Corrosion of Steel Reinforcement; Coefficient of Diffusion for Chloride Ions; Mineral Admixtures; Blast-furnace Slag Concrete
• Target Audience: 一般
• Note (General): 鉄筋コンクリート構造物の早期劣化の問題が指摘されて久しいが、厳しい塩分腐食環境下におかれた鉄筋コンクリート構造物では比較的短い期間に何らかの形で鉄筋腐食に伴う劣化・変状が現われてくるのが通常である。鉄筋コンクリート構造物の維持管理や補修法を決定するための検査法には、コンクリート中の鉄筋とかぶりコンクリートの状況を現場にてリアルタイムに把握できることが重要であり、また将来にわたる鉄筋腐食の進行を初期段階にて精度良く予測するには、かぶりコンクリートの塩化物イオン、酸素の透過性および鉄筋に対する保護機能を総合的に判断できる検査法が望まれている。このような観点より、(1)海洋環境下に暴露した鉄筋埋設コンクリート試験体の腐食状況および塩分浸透量を調べることにより、かぶりコンクリートの塩化物イオン透過性と内部鉄筋の腐食との関係について明らかにした。(2)交流インピーダンス法より求めたコンクリートの電気伝導率(比抵抗)と細孔構造との関係を詳細に調べることにより、コンクリートの電気伝導率(比抵抗)から塩化物イオンの透過性や鉄筋に対する保護機能などの性質を推定する方法の有効性について検証した。(3)急速塩化物イオン透過性試験(AASHTO T-227)はかぶりコンクリートの品質や補修材料の性能などの評価が迅速かつ簡単にできるのが特徴であるが。本試験法によるかぶりコンクリートの鉄筋腐食に対する防食性能の評価基準は適用するコンクリートの種類によって相違すると考えられるので、各種コンクリートに対して急速塩化物イオン透過性試験と交流インビーダンス法による電気伝導率(比抵抗)の測定を実施し、両者の関係について明らかにした。以上の結果をふまえて、かぶりコンクリートの鉄筋腐食に対する腐食機能の評価法および急速塩化物イオン透過試験の適用性についての提言を行った。; From the results of 5-year exposure test under a marine environment, it was confirmed that the fly ash 30% concrete and the silica fume 10% concrete performed better in corrosive behavior of the steel bar in concrete compared with the normal Portland cement concrete and the blast-furface slag 50% concrete, and that the results of the Rapid Chloride Permeability Test (RCPT,AASHTO T277) gave a reasonable estimate of chloride ion permeability of normal Portland cement concrete in service although the AASHTO T277 test was primarily a conductivity measurement. With the regard to the chloride ion permeability of concretes incorporating mineral admixtures, the results of the RCPT showed that both the surface and the interior of the concretes with mineral admixtures were much less permeable to chloride ions than the corresponding normal Portland cement concrete under all curing and environmental conditions. Furthermore, it was found that there was a good correlation between the charge passed in the RCPT,the initial direct current and the electrical resistance, which also correlated well with the chloride ion penetration depth into the concrete after the RCPT.With the regard to the diffusion coefficient for chloride ions calculated according to the Ficks second law, the coulomb values obtained from the RCPT also correlated well with both the diffusion coefficient for chloride ions and the depth of chloride ion penetration after the exposure to a marine environment.; 研究課題/領域番号:07650526, 研究期間(年度):1995-1996; 出典：「交流インピーダンス法によるコンクリートの鉄筋腐食の新しい検査法の開発」研究成果報告書 課題番号07650526(KAKEN：科学研究費助成事業データベース（国立情報学研究所）) 本文データは著者版報告書より作成
• DOI: 10.24517/00049880
• Source: https://kanazawa-u.repo.nii.ac.jp/?action=repository_action_common_download&item_id=43538&item_no=1&attribute_id=26&file_no=1
• Access Restrictions: 限定公開
• Rights (production): CC BY-NC-ND
• Related Material: https://kaken.nii.ac.jp/search/?qm=50115250; https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-07650526/; https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-07650526/076505261996kenkyu_seika_hokoku_gaiyo/
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 金沢大学 : 金沢大学学術情報リポジトリKURA