水素結合を有する低分子によるカーボンブラック充てん高分子複合材料の導電性制御

• Material Type: 文書・図像類
• Title: 水素結合を有する低分子によるカーボンブラック充てん高分子複合材料の導電性制御
• Author/Editor: 新田, 晃平; Nitta, Koh-Hei
• Author Heading: 新田, 晃平; Nitta, Koh-Hei
• Publication, Distribution, etc.: 金沢大学理工研究域フロンティア工学系
• Publication Date: 2004-03
• Publication Date (W3CDTF): 2004-03
• Alternative Title: Molecular mobility and conductivity in polymeric hybrids hydrogen-bonding with some inorganic fillers such as carbon black, and hindered phenol and amine conpounds
• Periodical title: 平成15(2003)年度 科学研究費補助金 基盤研究(C) 研究成果報告書 = 2003 Fiscal Year Final Research Report
• No. or year of volume/issue: 2001-2003
• Volume: 2001-2003
• Pages: 5p.-
• Text Language Code: jpn
• Subject Heading: 塩素化ポリエチレン; 複合材料; ヒンダードフェノール; ヒンダードアミン; 水素結合; 動的粘弾性; 応力緩和; Chlorinated polyethylene; Composite materials; Hindered phenol; Hindered amine; Hydrogen bond; Dynamic viscoelasticity; Stress relaxation
• Target Audience: 一般
• Note (General): 本研究は、この複合導電材料の方位に着目して、極性低分子化合物の水酸基と、樹脂がもつ酸素基との間に水素結合を形成させることにより、その場で低分子粒子を高分子マトリックスに分散させ、低分子の形や大きさなどにより導電性を支配する因子を割り出すことを行った。その導電性と直接関わる基礎的な知見を得るために、上記の導電性と密接に関係する極性低分子と高分子との水素結合に基づく分子間相互作用を明らかした。極性低分子としてヒンダードフェノールやヒンダードアミン等の極性低分子との混合系を調べた結果、マトリックス樹脂を極性低分子の間の水素結合が発生し、水素結合が分子運動性に大きく、影響を及ぼし室温領域に巨大な緩和分散を発現させることがわかった。また、延伸過程中で水素結合の組換えがおこり材料の運動性が変化することも分かった。その結果、水素結合の強弱によって分子運動性が大きく影響され、さらにはバルクの力学特性に大きく影響を及ぼすことが分かった。さらに、シリカゲルを分散材として用いた場合の分散状態と分子運動性の変化を調べた。この分子運動性は導電性と密接に関係する。シリカ微粒子と塩素化ポリエチレンが熱処理によって化学結合することがわかった。これは、これまでの水素結合により強い分散材とさらに母体材料として結晶性高分子固体であるポリプロピレンをもちいシリカゲル微粒子のとマトリックスとの相互作用をもった複合材料になることが判明した。以上の結果より、これまでほとんど困難であった樹脂の分子運動性や極性分散在の凝集状態を制御できることがわかった。今後、この成果を基礎知見として導電性のみならず応力の伝播機構やガス透過機構などの輸送現象全般の制御方法への展開を予定している。; Dynamic mechanical properties and microstructure of an organic hybrid consisting of chlorinated polyethylene(CPE) and inorganic fillers such as carbon blacks, hindered phenol, hindered amine, and silica particles with some polar groups were investigated. In order to clarify the effects of hydro bond on molecular mobility of CPE, the hindered phenol and amine were added to CPE matrix. The fillers clearly exhibited two second-order transitions at 6 and 69℃ in addition to the melting : the transition at lower temperature is assigned to the glass transition. and the transition at higher temperature is considered to be caused by the dissociation of hydrogen bond between the hydroxyl groups of the fillers. When blending with CPE, part of the fillers molecules was dispersed into the CPE matrix, and most of them formed an filler-rich phase. As a result, a novel transition appeared above the glass-transition temperature of the CPE matrix. It was assigned to the dissociation of the intermolecular hydrogen bond between the a-hydrogen of CPE and the hydroxyl groups of fillers within the AO-80-rich phase. Dynamic mechanical properties and microstructure of CPE/filler hybrid were capable of being controlled by the thermal treatment. Consequently, the CPE/filler hybrid is a good damping material and shows a shape memory effect.; 研究課題/領域番号:13650746, 研究期間(年度):2001-2003; 出典：「水素結合を有する低分子によるカーボンブラック充てん高分子複合材料の導電性制御」研究成果報告書 課題番号13650746 (KAKEN：科学研究費助成事業データベース（国立情報学研究所）) 本文データは著者版報告書より作成
• DOI: 10.24517/00052632
• Source: https://kanazawa-u.repo.nii.ac.jp/?action=repository_action_common_download&item_id=46299&item_no=1&attribute_id=26&file_no=1
• Access Restrictions: 限定公開
• Rights (production): CC BY-NC-ND
• Related Material: https://kaken.nii.ac.jp/search/?qm=70260560; https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-13650746/; https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-13650746/136507462003kenkyu_seika_hokoku_gaiyo/
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 金沢大学 : 金沢大学学術情報リポジトリKURA