組紐技術を応用した内部隔壁を有する中空材FRPプリフォームの創成

Material type: 文書・図像類

Author: 喜成, 年泰ほか

Publisher: 金沢大学理工研究域機械工学系

Publication date: 2021-06-09

Material Format: Digital

Capacity, size, etc.: -

NDC: -

View All

Notes on use

Note (General)：: 連続炭素繊維を熱可塑性樹脂に予め含浸しテープ状に細くスリットしたテープ（以下CFRTPテープ）を用い、組紐形成時においてテープが中空円筒表面を隙間なく覆い、折れ曲がることがないような編組条件を探索し、熱間プレスした試料を作成し、曲げ強度で800MPa、曲げ弾性率で100GPaを超えるCFRTPパイプ...

Related materials as well as pre- and post-revision versions

https://kaken.nii.ac.jp/search/?qm=90195321

https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-18K03869/

https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-18K03869/18K03869seika/

Search by Bookstore

Holdings of Libraries in Japan

This page shows libraries in Japan other than the National Diet Library that hold the material.

List of Cooperating Institutions and Databases

Please contact your local library for information on how to use materials or whether it is possible to request materials from the holding libraries.

other

Kanazawa University Repository for Academic Resources
Digital
You can check the holdings of institutions and databases with which 学術機関リポジトリデータベース（IRDB）（機関リポジトリ） is linked at the site of 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）.
Kanazawa University Repository for Academic Resources

Search by Bookstore

Bibliographic Record

You can check the details of this material, its authority (keywords that refer to materials on the same subject, author's name, etc.), etc.

Digital

Material Type: 文書・図像類
Title: 組紐技術を応用した内部隔壁を有する中空材FRPプリフォームの創成
Author/Editor: 喜成, 年泰
Kinari, Toshiyasu
Author Heading: 喜成, 年泰
Kinari, Toshiyasu
Publication, Distribution, etc.: 金沢大学理工研究域機械工学系
Publication Date: 2021-06-09
Publication Date (W3CDTF): 2021-06-09
Alternative Title: Creating hollow preform for FRP with braiding
Periodical title: 令和2(2020)年度科学研究費補助金基盤研究(C) 研究成果報告書 = 2020 Fiscal Year Final Research Report
No. or year of volume/issue: 2018-04-01 - 2021-03-31
Volume: 2018-04-01 - 2021-03-31
Pages: 12p.-
Text Language Code: jpn
Subject Heading: 炭素繊維強化複合材料
組紐
炭素繊維
熱可塑性樹脂
中立糸
機械的性質
プリフォーム
Target Audience: 一般
Note (General): 連続炭素繊維を熱可塑性樹脂に予め含浸しテープ状に細くスリットしたテープ（以下CFRTPテープ）を用い、組紐形成時においてテープが中空円筒表面を隙間なく覆い、折れ曲がることがないような編組条件を探索し、熱間プレスした試料を作成し、曲げ強度で800MPa、曲げ弾性率で100GPaを超えるCFRTPパイプを得ることができた。この成果は当初目的の「同一質量の鋼構造物と比較して5倍以上の機械的強度」に対して、鋼の比重7.8、CFRPの比重1.5を勘案すると、曲げ強度において目標を大きく上回ることができた。
Braid-press forming was developed for manufacturing hollow tube parts made of carbon fiber reinforced thermoplastic (CFRTP) tape. The CFRTP tapes were manufactured by slitting Uni Direction sheet which impregnate opened continuous carbon fibers along the fiber axis with thermoplastic resin into tape form thin. They were braided to make a tube, which was consolidated under pressure and heat in the press forming process. At the braid formation, braiding tapes and the middle end tapes covered up emptiness cylinder surface without a gap.The mechanical properties of the obtained pipes were larger than 800 MPa in bending strength and were larger than 100 GPa in bending modulus. These results greatly exceeded the original purpose, ‘the mechanical strength that was more than 5 times compared with the steel structure of the same mass.’
研究課題/領域番号:18K03869, 研究期間(年度):2018-04-01 - 2021-03-31
出典：「組紐技術を応用した内部隔壁を有する中空材ＦＲＰプリフォームの創成」研究成果報告書　課題番号18K03869（KAKEN：科学研究費助成事業データベース（国立情報学研究所））（https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-18K03869/18K03869seika/）を加工して作成
DOI: 10.24517/00057851
Source: https://kanazawa-u.repo.nii.ac.jp/?action=repository_action_common_download&item_id=51548&item_no=1&attribute_id=26&file_no=1
https://kanazawa-u.repo.nii.ac.jp/?action=repository_action_common_download&item_id=51548&item_no=1&attribute_id=26&file_no=1
Access Restrictions: 限定公開
Rights (production): CC BY-NC-ND
Related Material: https://kaken.nii.ac.jp/search/?qm=90195321
https://kaken.nii.ac.jp/grant/KAKENHI-PROJECT-18K03869/
https://kaken.nii.ac.jp/report/KAKENHI-PROJECT-18K03869/18K03869seika/
Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）
https://irdb.nii.ac.jp
Original Data Provider (Database): 金沢大学 : 金沢大学学術情報リポジトリKURA