照射リグ(II-06)及びサーベイランスバックアップ材の照射後試験(2) : 第3報 炉容器相当材(母材及び溶接継手)のクリープ試験

• Material Type: 文書・図像類
• Title: 照射リグ(II-06)及びサーベイランスバックアップ材の照射後試験(2) : 第3報 炉容器相当材(母材及び溶接継手)のクリープ試験
• Author/Editor: 菊地 隆雄; 岡 裕; 谷 賢; 石原 幹也
• Author Heading: 菊地 隆雄; 岡 裕; 谷 賢; 石原 幹也
• Publication Date: 1985-11
• Publication Date (W3CDTF): 1985-11
• Alternative Title: Post-irradiation test on reactor vessel material irradiated in surveillance test rig (II-06); 3. Creep rupture test on reactor vessel material
• Periodical title: PNC TN941 85-163
• Text Language Code: jpn
• Target Audience: 一般
• Note (General): 「常陽」炉容器サーベイランス材のバックアップ試験の一環として「常陽」燃料貯蔵ラック位置(R11)で75MW,1サイクルの間照射した炉容器相当材の母材及び溶接継手について500$^{\circ}C$でクリープ破断試験を行った。また同時に同照射リグを用いて安全棒の駆動機構に用いられるスプリングの照射による特性変化の基礎データを得ることを目的としてインコネルX750及びインコネル718製のスプリングを圧縮荷重負荷の状態で照射し,照射後,外観観察,寸法測定,バネ定数測定,金相試験を実施した。照射量は1.0$\sim$1.5$\times$10$\times$19n/cm$\times$2(E$>$0.1MeV),4.6$\times$10$\times$6n/cm$\times$2(E$<$0.4eV),1.8$\times$10$\times$20n/cm$\times$2(total)で,照射温度は420$^{\circ}C$$\sim$470$^{\circ}C$であった。▲1.炉容器相当材のクリープ破断試験結果▲照射した母材のクリープ破断伸び及び断面収縮率は破断時間が長い場合は受入材よりも低くなる傾向を示した。母材のクリープ破断伸び及び断面収縮率は破断寿命が$\sim$5000h程度の場合に照射の有無によらず16\%以上の値を示している。▲溶接継手のクリープ破断強度に及ぼす照射の影響は傾向的には母材の場合とはぼ同じである。未照射材の破断位置は溶接金属部であるが照射材では母材部である。破断伸びは照射により低下し,その値は母材より小さい。▲「常陽」構造設計指針の500$^{\circ}C$におけるクリープ破断応力強さの最小値に対して本実験材は上回っている。▲2.スプリングの試験結果▲インコネルX750製スプリングの全長は照射前に比べて最も変化の著しいもので30\%短くなったが,インコネル718製スプリングの全長にはほとんど変化が見られなかった。いずれのスプリングも照射によるバネ定数の変化は見なれなかった。▲; As one of the back-up tests for the structural material surveillance program of the "JOYO" reactor vessel, creep rupture tests at 500$^{\circ}$C were performed on a SUS304 stainless steel plate material and its welded joint, similar to the reactor vessel material. The specimens were irradiated in a ffuel storage rack (R11) of the "JOYO" for one cycle at the power of 75MW. The irradiation rig also contained stressed spring specimens of Inconel X-750 and Inconel 718 to examine irradiation effects on the driving force of safety rods. 1.Creep rupture tests on the similar one to the "JOYO" reactor vessel material. Creep rupture strength of base metal decreased after irradiation when the time to rupture was over 1400h. The values of creep rupture elongation and reduction of area for both irradiated and unirradiated materials were more than 16\% at least even after creep rupture test of 5000h. The influence of irradiation on the creep rupture strength of welded joint was similar to the effect for base metal. While the fracture position of unirradiated weld joint was located at the weld metal portion, that of irradiated one was base metal. The rupture elongation of weld joint, which decreased by irradiation, was smaller than that of base metal. The creep rupture strength obtained at 500$^{\circ}$C was slightly larger than the minimum stress intensity to rupture values for SUS304 in design guide for the "JOYO". 2.Test results for spring. The length of Inconel X-750 spring were shortened by 30\% at most after irradiation, While that of Inconel 718 spring did not change. The spring constant of bath springs did not changed by irradiation.
• Source: /PNC-TN941-85-163.pdf （fulltext）; https://jopss.jaea.go.jp/pdfdata/PNC-TN941-85-163.pdf
• Access Restrictions: 限定公開
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 日本原子力研究開発機構 : JOPSS:JAEA Originated Papers Searching System

• Summary, etc.: 「常陽」炉容器サーベイランス材のバックアップ試験の一環として「常陽」燃料貯蔵ラック位置(R11)で75MW,1サイクルの間照射した炉容器相当材の母材及び溶接継手について500$^{\circ}C$でクリープ破断試験を行った。また同時に同照射リグを用いて安全棒の駆動機構に用いられるスプリングの照射によ...