「常陽」MK-I炉心燃料(PPJD2B)の照射後試験(2); ラッピングワイヤの試験

• Material Type: 文書・図像類
• Title: 「常陽」MK-I炉心燃料(PPJD2B)の照射後試験(2); ラッピングワイヤの試験
• Author/Editor: 谷 賢; 吉持 宏; 関 成一; 多田 薫; 田地 弘勝; 一海 俊景
• Author Heading: 谷 賢; 吉持 宏; 関 成一; 多田 薫; 田地 弘勝; 一海 俊景
• Publication Date: 1981-07
• Publication Date (W3CDTF): 1981-07
• Alternative Title: Post-irradiation examination on the wrapping wire used in "JOYO" MK-I core (Subassembly PPJD2B)
• Periodical title: PNC TN941 81-142
• Text Language Code: jpn
• Target Audience: 一般
• Note (General): 高速実験炉「常陽」の炉心構成要素の健全性を確認し,また高速炉用炉心材料の基礎的な照射データを得るための試験計画の一環として,「常陽」炉心で出力75MWで使用されたラッピングワイヤの照射後試験を行った。今回試験したラッピングワイヤは集合体PPJD2Bに組み込まれて使用されたもので,照射温度は370$\sim$510$^{\circ}C$,最大照射量は3.07$\times$10$\times$22n/cm$\times$2(E$>$0.1MeV)であった。照射後試験は外径測定,密度測定,金相試験及び硬さ試験の各項目について行い,その結果をPPJD1A(最大照射量2.6$\times$10$\times$21n/cm$\times$2),PPJX08(同9.6$\times$10$\times$21n/cm$\times$2),PPJX14(同1.5$\times$10$\times$21n/cm$\times$2),PPJX06(同2.0$\times$10$\times$22n/cm$\times$2)及びPPJX11(同2.7$\times$10$\times$22n/cm$\times$2)のラッピングワイヤの試験結果とあわせて検討した。主な結果は次のとおりである。Reference試料に比較し,照射材の外径は最大0.3\%程度増加し,密度は最大0.6\%程度低下していた。軸方向3ケ所から採取した各試料について,密度測定結果から算出した体積変化($\Delta$V/V)と外径変化の3倍(3$\Delta$D/D)はかなりよく一致していた。このことから,ラッピングワイヤのスウェリングが発生したものと考えられる。金相試験において結晶拉界に炭化物の析出がみられた。硬さは受入材にくらべ最高Hv=170程度増加していた。; To make sure that the core materials of the fast experimental reactor "JOYO" are in safety conditions and to get basic knowlege about the behavior of FBR core materials after irradiation, post-irradiation examinations on wrapping wires (SUS316, annealed) were carried out. The wrapping wires were fabricated into the subassembly PPJD2B and irradiated at 370 $\sim$ 510$^{\circ}$C up to the neutron fluence of 3,07 $\times$ 10$^{22}$ n/cm$^{2}$ (E$>$0.1 Mev). Diameter measurement, density measurement, metallurgical test and hardness test were performed and compared with the previous data. The results obtained are summarized as follows. (1)Maximum diameter increase of 0.3\% and maximum density decrease of 0.6\% were observed. (2)$\Delta$V/V corresponds well to 3$\Delta$D/D, which indicates the swelling of wrapping wires. (3)Precipitation of carbide was observed on grain boundaries. (4)Maximum hardness increase of Hv=170 was observed.
• Source: /PNC-TN941-81-142.pdf （fulltext）; https://jopss.jaea.go.jp/pdfdata/PNC-TN941-81-142.pdf
• Access Restrictions: 限定公開
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 日本原子力研究開発機構 : JOPSS:JAEA Originated Papers Searching System

• Summary, etc.: 高速実験炉「常陽」の炉心構成要素の健全性を確認し,また高速炉用炉心材料の基礎的な照射データを得るための試験計画の一環として,「常陽」炉心で出力75MWで使用されたラッピングワイヤの照射後試験を行った。今回試験したラッピングワイヤは集合体PPJD2Bに組み込まれて使用されたもので,照射温度は370$\...