真空中高温における自己潤滑性複合材のトライボロジー特性に及ぼす相手材の影響

• Material Type: 文書・図像類
• Title: 真空中高温における自己潤滑性複合材のトライボロジー特性に及ぼす相手材の影響
• Author/Editor: 鈴木, 峰男; 森山, 稔; 西村, 允; 長谷川, 正二; Suzuki, Mineo; Moriyama, Minoru; Nishimura, Makoto; Hasegawa, Masaji
• Author Heading: 鈴木, 峰男; 森山, 稔; 西村, 允; 長谷川, 正二; Suzuki, Mineo; Moriyama, Minoru; Nishimura, Makoto; Hasegawa, Masaji
• Publication, Distribution, etc.: 航空宇宙技術研究所
• Publication Date: 1993-02
• Publication Date (W3CDTF): 1993-02
• Alternative Title: Effect of counterpart materials on tribological performance of selflubricating composites evaluated at high temperature in a vacuum
• Periodical title: 航空宇宙技術研究所報告 = Technical Report of National Aerospace Laboratory
• No. or year of volume/issue: 1192
• Volume: 1192
• Pages: 1-22
• ISSN (Periodical Title): ISSN : 0389-4010
• Text Language Code: jpn
• Subject Heading: 自己潤滑性複合材料; 高温; 真空; トライボロジー; 窒化けい素; 2硫化モリブデン; 酸化モリブデン; ニオブ; ホットプレス; 摩耗; 耐摩耗性; ステンレス鋼; SUS304; 工具鋼; ピンオンディスク摩擦試験; selflubricating composite; high temperature; vacuum; tribology; silicon nitride; molybdenum disulfide; molybdenum oxide; niobium; hot press; wear; wear resistance; stainless steel; tool steel; pin on disk friction test
• Target Audience: 一般
• Note (General): MoS2,MoO2,Nbから成る自己潤滑性複合材料、およびこれにSUS304をさらに添加した複合材料をピン試験片として用い、真空中、450度Cまでの温度でピン/円板型の摩擦試験を行なった。相手円板材料は窒化珪素(Si3N4)、3種の工具鋼(M-50,SK-3,SKD-11)、ステンレス鋼(SUS304)について試験した。相手材がSi3N4の場合、真空中、450度Cまでの高温下できわめて良好なトライボロジー特性を示した。また、相手材がM-50の場合でも優れた耐摩耗性を示した。相手材がSUS304、焼入れしていないSK-3やSKD-11などのように硬度が低い場合には、複合材とともに相手材にも多量の摩耗が発生した。しかし、焼入れにより相手材を硬くすると、複合材、相手鋼ともに摩耗量は大幅に低下した。表面が硬くかつ軽移膜が強固に付着する相手材がこの複合材に適していると推測した。SUS304を添加した複合材は無添加の場合に比べ強度が向上するとともに、相手材がSi3N4の場合にはトライボロジー特性も改善された。適した相手材と組合わせることにより、この複合材は、今後、高温・真空中での用途に有望である。; Pin-on-disk friction tests were carried out at temperatures up to 450 C in a vacuum using a self lubricating composite pin. The composites used were molybdenum disulphide (MoS2) + molybdenum dioxide (MoO2) + niobium (Nb), and MoS2 + MoO2 + Nb + stainless steel (SUS304). Tested disk materials were silioon nitride (Si3N4), three types of tool steel (M-50, SK-3 and SKD-11) and stainless steel (SUS304). When the counterpart material was Si3N4, excellent tribological performance was obtained at high temperatures up to 450 C in a vacuum. Good wear resistance was also obtained with an M-50 tool steel disk. In both cases, a thin transfer film was formed on the disk surface from the composite pin. A considerable amount of wear, for both the composite pin and steel disks, was observed when the disks had a low hardness, such as SUS304 disk, and not-hardened SK-3 and SKD-11 disks. With SK-3 and SKD-11 disks, hardening the disk was effective in decreasing wear of both the pin and the disk. The results indicated that a counterpart material which had a fairly hard surface and developed a thin, adherent transfer film was essential to obtain good tribological performance. Addition of SUS304 to the composite improved strength, and also improved tribological performance when slid against an Si3N4 disk. The composites, with appropriate counterpart materials, have potential high temperature vacuum applications.; 資料番号: AA0004207000; レポート番号: NAL TR-1192
• Source: https://jaxa.repo.nii.ac.jp/?action=repository_action_common_download&item_id=41177&item_no=1&attribute_id=31&file_no=1
• Access Restrictions: 限定公開
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 宇宙航空研究開発機構 : 宇宙航空研究開発機構リポジトリ