カーボン/ポリイミド(T800H/PMR-15) 複合材料Hot/Wet圧縮強度に及ぼす吸水の影響

• Material Type: 文書・図像類
• Title: カーボン/ポリイミド(T800H/PMR-15) 複合材料Hot/Wet圧縮強度に及ぼす吸水の影響
• Author/Editor: 濱口, 泰正; 下河, 利行; 加藤, 久弥; Hamaguchi, Yasumasa; Shimokawa, Toshiyuki; Kato, Hisaya
• Author Heading: 濱口, 泰正; 下河, 利行; 加藤, 久弥; Hamaguchi, Yasumasa; Shimokawa, Toshiyuki; Kato, Hisaya
• Publication, Distribution, etc.: 航空宇宙技術研究所
• Publication Date: 2000-10
• Publication Date (W3CDTF): 2000-10
• Alternative Title: Effect of moisture absorption on hot/wet compressive strength of T800H/PMR-15 carbon/polyimide
• Periodical title: 航空宇宙技術研究所報告 = Technical Report of National Aerospace Laboratory
• No. or year of volume/issue: 1413
• Volume: 1413
• Pages: 1-13
• ISSN (Periodical Title): ISSN : 0389-4010
• Text Language Code: jpn
• Subject Heading: カーボン/ポリイミド複合材料; 吸水性; hot/wet圧縮強度; 擬似等方積層材料; 圧縮破壊モード; 統計的性質; トラベラークーポン; 残留含水率; 脱水率; 試験片厚さ; 高温圧縮試験; carbon polyimide composite material; moisture absorption property; hot wet compressive strength; quasi isotropic stacking sequence; compression fracture mode; statistical property; traveler coupon; residual moisture content; moisture desorption; specimen thickness; high temperature compression test
• Target Audience: 一般
• Note (General): 本研究の目的は、T800H/PMR-15カーボン/ポリイミド複合材料で製作した擬似等方積層材料のHot/Wet圧縮強度の評価であり、ここでは、Hot/Wet圧縮強度に及ぼす吸水量の影響について統計的に調べた。吸水率を1.2wt%、1.4wt%および1.8wt%に設定した試験片の圧縮強度試験を260度C高温環境で実施した。これらの試験から、圧縮破壊モード、Hot/Wet圧縮強度に及ぼす吸水率の影響、Hot/Wet圧縮強度の統計的性質およびB許容値、試験片の吸水率をモニターするトラベラークーポンの有効性、試験片厚さとHot/Wet圧縮強度の相関関係を明らかにした。主な試験結果は、(1)Hot/Wet圧縮強度は、試験直後に計測した残存吸水率と良好な相関関係を示した。(2)Hot/Wet圧縮強度の変動係数は、室温/Dry条件における圧縮強度の変動係数の2倍であった。; The objective of this study is to statistically investigate the effect of moisture absorption on the hot/ wet compressive strength of a T800H/PMR-15 carbon/polyimide composite with a quasi-isotropic stacking sequence. Compression tests on moisture absorbed specimens were conducted at 260 C. These tests clarified the compression fracture mode, the effect of moisture absorption on the hot/ wet compressive strength, statistical properties and a design allowable of hot/wet compressive strength, the effectiveness of a traveler coupon in monitoring moisture absorption, and the relationship between specimen thickness and hot/wet compressive strength. Important results were as follows: (1) hot/wet compressive strength was found to be closely related to residual moisture content measured immediately after the test; and (2) the coefficient of variation of hot/wet compressive strength was found to be approximately twice as large as that of room temperature/dry compressive strength.; 資料番号: AA0028658000; レポート番号: NAL TR-1413
• Source: https://jaxa.repo.nii.ac.jp/?action=repository_action_common_download&item_id=41482&item_no=1&attribute_id=31&file_no=1
• Access Restrictions: 限定公開
• Data Provider (Database): 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• Original Data Provider (Database): 宇宙航空研究開発機構 : 宇宙航空研究開発機構リポジトリ