Bibliographic Record
You can check the details of this material, its authority (keywords that refer to materials on the same subject, author's name, etc.), etc.
- Material Type
- その他
- Author/Editor
- 吉川, 明彦
- Publication Date
- 2005-03
- Publication Date (W3CDTF)
- 2005
- NDC
- Target Audience
- 一般
- Note (General)
- 出版タイプ： NA研究種目:基盤研究(B) 研究種目コード:310研究課題番号:13450121審査分野:一般 区分コード:03本年は、本研究の最終年度として、InNをベースとした光・電子デバイス構造実現へのステップとして、N極性における高In組成のInGaNおよびAlInN三元混晶のエピタキシ制御とInNをベースとした多重量子井戸(MQW)の検討を進めた。また、大きな格子不整合に起因するヘテロ界面での転位や欠陥の影響を避けうる構造として、量子ドット構造の形成についての検討も進めた。(1)InNをベースとした三元混晶作製:InGaN及びAlInNエピタキシをN極性にて成膜することにより、全In組成域での成膜が可能となった。特にAlInNについては、世界で初めて広い組成領域でのエピ膜が得られ、この混晶系でのボーイングパラメータが約3.8eVと従来報告値より大きいことを明らかにした。(2)InNをベースとしたMQWの作製:まずInN/GaN系でのMQW作製を検討した。N極性での高い成膜温度実現により、MQW構造は形成できたが約16%の大きな格子不整合に起因し、X線サテライトピークの観察は不可能であった。一方、障壁層をInGaNおよびInAlNとすることは格子不整合軽減にきわめて効果的であり、断面TEMおよびHR-XRD評価で高品質のMQW実現を確認した。特にAlInNは大きな伝導帯不連続を保ちながら格子不整合低減を可能とするものであることを示した。(3)InNドットの作製:N極性でのInN量子ドット作製に初めて成功し、その形成機構を詳しく検討した。以上より、窒化物系化合物半導体のエピタキシ制御と物性制御において、結晶極性制御がきわめて重要であることを明らかにした。別刷論文(p.15-264)削除平成13年度～平成16年度科学研究費補助金(基盤研究(B)(2))研究成果報告書
- Access Restrictions
- インターネット公開