Ti合金(SP700)及びSiC(SCS-6)/Ti(SP700)複合材料の引張試験

• 資料種別: 文書・図像類
• タイトル: Ti合金(SP700)及びSiC(SCS-6)/Ti(SP700)複合材料の引張試験
• 著者・編者: 祖父江, 靖; 橋本, 良作; 小河, 昭紀; Zhou, Fenghua; Sofue, Yasushi; Hashimoto, Ryosaku; Ogawa, Akinori
• 著者標目: 祖父江, 靖; 橋本, 良作; 小河, 昭紀; Zhou, Fenghua; Sofue, Yasushi; Hashimoto, Ryosaku; Ogawa, Akinori
• 出版事項: 航空宇宙技術研究所
• 出版年月日等: 1999-09
• 出版年（W3CDTF）: 1999-09
• 並列タイトル等: Tensile tests of SiC/Ti composites and SP700 titanium alloy
• タイトル（掲載誌）: 航空宇宙技術研究所資料 = Technical Memorandum of National Aerospace Laboratory
• 巻号年月日等（掲載誌）: 742
• 掲載巻: 742
• 掲載ページ: 1-19
• ISSN（掲載誌）: ISSN : 0452-2982
• 本文の言語コード: jpn
• 件名標目: 航空機エンジン材料; チタン合金; 炭化けい素チタン複合材料; SP700; SCS-6; 引張試験; 引張強さ; 引張破壊; 応力ひずみ特性; 弾性率; ポアソン比; 破断伸び; HIP成形; 高温静水圧圧縮; aircraft engine material; titanium base alloy; silicon carbide titanium composite; SCS 6; tensile test; tensile strength; tensile fracture; stress strain characteristic; elastic modulus; Poisson's ratio; rupture elongation; HIP forming; hot isostatic pressing
• 対象利用者: 一般
• 一般注記: 航空エンジンの軽量化を目的に、SiC/Ti複合材料を構造部材に適用することの可能性を検討した。SiC/Ti複合材料とマトリックスであるTi合金の機械的特性を把握するため、Ti合金およびSiC/Ti複合材料の常温の引張試験を行い、引張強さ、弾性率、ポアソン比、破断伸びなどの材料強度特性を調べた。試験片の種類は、(1)HIP(高温静水圧圧縮)成形のTi合金(SP700)試験片、(2)圧延成形のTi合金(SP700)試験片、および(3)HIP成形のSiC(SCS-6)/Ti合金(SP700)複合材試験片の3種類である。引張破壊後の試験片について光学顕微鏡を用いて破断部、走査電子顕微鏡を用いて破面の観察を行った。本報では、これらの結果について述べた。; Tensile tests of titanium alloy and SiC/Ti composites at room temperature were carried out to examine the strength characteristics of the materials. Before testing, finite element analysis was performed to confirm that no stress concentration exists on the present two shapes of specimens. Three types of material were used in the tensile tests SP700 titanium alloy manufactured by Hot Isostatic Pressing (HIP) forming, SP700 titanium alloy manufactured by roll forming, and SiC/Ti composites manufactured by HIP forming. In each test, tensile strength characteristics were measured, including tensile strength, elongation, elastic modulus and Poisson's ratio. After testing, the rupture area of each specimen was observed by optical microscope, and the fractured surface by scanning electron microscope. All the testing data and photographs were synthesized for this paper.; 資料番号: AA0001967000; レポート番号: NAL TM-742
• オンライン閲覧公開範囲: 限定公開
• 掲載誌（NCID）: AN00314334; https://ci.nii.ac.jp/ncid/AN00314334
• 連携機関・データベース: 国立情報学研究所 : 学術機関リポジトリデータベース（IRDB）（機関リポジトリ）; https://irdb.nii.ac.jp
• 提供元機関・データベース: 宇宙航空研究開発機構 : 宇宙航空研究開発機構リポジトリ