Author/EditorESRAA MOHAMED ELMOATASEM IBRAHIM ELKHODARY
Alternative Titleポリ乳酸ステレオコンプレックス形成に及ぼす成分ポリマーの分子量と混合条件の影響および耐熱性ポリ乳酸二軸延伸フィルムの構造物性
Note (General)Thesis Abstract (In approx. 300 English words) Blends of poly(L-lactic acid) (PLLA) and poly(D-lactic acid) (PDLA) forms stereocomplex crystal (sc) which shows a melting point around 230oC, about 50oC higher than that of PLLA and PDLA homo crystal (hc). The degree of sc is affected by the method and condition of mixing, the optical purity and the molecular weight of parent poly(lactide)s, and by the mixing ratio. Among these factors, the effects of the molecular weight of parent polymers and the mixing condition on the stereocomplexation of the equal bends of PLLA and PDLA are determined in this study. Further the effect of the processing condition on the physical property and the higher-order structure of the biaxially oriented PLLA/PDLA blend films were studied. The effect of the molecular weight on the hc crystallization of PLLAs is those known for various semi-crystalline polymers. However there are both lower and higher threshold of the molecular weight exist for sc crystallization. Lower threshold of the molecular weight for the sc crystallization of PLLA/PDLA blend is about 1,000, while that for hc crystallization of PLLA is about 2,500. When the molecular weight is higher than 25,000, both hc and sc tended to form in the blend. The effect of the mixing condition on the sc formation of the PLLA/PDLA blends was investigated. The blends melt-mixed at 200oC and 210oC under application of a high shear flow tend to show a single melting peak of the sc. Further kneading of the blends at an elevated temperature caused the transesterification between the same enatiomeric chains forming block copolymers of L- and D-chains. This block copolymer acts as a nucleating agent of sc and the compatibilizing agent between PLLA and PDLA and promotes the formation of SC. PLLA/PDLA blend was prepared at an optimum condition. The blend was compression molded into films and biaxially drawn and annealed. The biaxially drawn films showed a broad crystalline WAXD reflection and the application of annealing completely changed the reflections into those of sc. The mechanical property was improved by the biaxial drawing and the annealing for short period of time.
Collection (particular)国立国会図書館デジタルコレクション > デジタル化資料 > 博士論文
Date Accepted (W3CDTF)2020-07-06T20:31:19+09:00
Data Provider (Database)国立国会図書館 : 国立国会図書館デジタルコレクション