The multiple evaluations of the influence oflight conditions to “Touch and cure" resin cements - in terms of bond strength test, in situ microhardness test and Raman spectroscopy

• Material Type: 博士論文
• Title: The multiple evaluations of the influence oflight conditions to “Touch and cure" resin cements - in terms of bond strength test, in situ microhardness test and Raman spectroscopy
• Author/Editor: PIMPINEE, EAMSA-ARD
• Author Heading: PIMPINEE, EAMSA-ARD
• Publication, Distribution, etc.: Hokkaido University
• Publication Date: 2020-03-25
• Publication Date (W3CDTF): 2020-03-25
• Alternative Title: “Touch and cure”システム型レジンセメントに対する光照射条件の影響についての多面的検討 - 接着試験, in situ マイクロ硬さ試験およびラマン分光法による重合測定を用いて
• Contributor: 佐野, 英彦; 井上, 哲; 吉田, 靖弘
• Degree grantor/type: 北海道大学
• Date Granted: 2020-03-25
• Date Granted (W3CDTF): 2020-03-25
• Dissertation Number: 甲第13864号
• Degree Type: 博士(歯学)
• Conferring No. (Dissertation): 甲第13864号
• Text Language Code: eng
• NDC: 497
• Target Audience: 一般
• Note (General): Recently, the new and novel “Touch and cure” technology for dual-cured resin cement was developed and introduced. This new technology is claimed that the polymerization reaction would start immediately after the mixed cement touching dentin surface. This dentin surface is already applied with the primer, containing the new unique added chemical polymerization initiator, before activated by using the light-curing unit. This study was aimed to evaluate the effect of light and dark conditions to two “Touch and cure” type and one conventional type dual-cured resin cements, in terms of bond strength testing. Nanoindentation microhardness and microRaman spectroscopies were also performed and analyzed to the light condition. 42 flat dentin surfaces polished with #600-SiC were prepared from caries-free human molars and premolars. Then randomly assigned into 3 tests, 1) microtensile bond strength (μTBS), 2) microhardness, and 3) degree of conversion (DC) analysis. 1) For μTBS, 30 molars were randomly divided into three groups: 1. G-CEM ONE (CS), 2. Panavia V5 (PV), both are “Touch and cure” resin cement, 3. RelyX Ultimate (RX); and further divided into two subgroups (n=5) according to light condition for cementation: 1. cement was light-cured from 5 directions for 20 seconds each (L), 2. cement was left in the darkroom for 30 min (D), auto-cured mode. 4-mm resin cement was built-up and cured with each light condition (L or D). Teeth were kept at 37oC, 24-h storage in distilled water, using a dark box for D-condition. 1 mm2 non-trimmed beams were tested for μTBS, expressed in MPa. The data were statistically analyzed by Games-Howell test (α=0.05). 2) For microhardness, premolars were cut, smear-layers were prepared and cement built-up and 24 h-water storage same as the μTBS specimen preparation in L-condition previously described. The teeth were cut perpendicular to the resin-dentin interface, 1 mmthickness slab, and polished with SiC paper and diamond paste down to 1 μm particle size. The microhardness data were evaluated by using the nanoindentation testing machine after specimens polishing 3 and 72 h. The indentation was tested four spots at each 20 μm interval distance from the resin-dentin interfaces until 200 μm. Games-Howell test was used for analyzing the mean values of each group. (α=0.05) 3) For DC analysis by microRaman spectroscopy, the testing slabs were cut and prepared and tested at 3 and 72 h, the same as the microhardness specimens. Each specimen, three lines (1 μm apart) were employed for evaluation Each line started at 2 μm from the resin-dentin interface and tested twenty spots having 1-10μm intervals until 60μm interface distance. One-way ANOVA and Tukey test were used for analyzing means values from each group (α=0.05). Correlation between DC and distance from the resin-dentin interface was analyzed by Spearman’s and Pearson’s correlation. 4) The fracture analysis of μTBS beams after testing was observed and analyzed by SEM. The resin-dentin interface was further investigated by TEM. Filler distribution of cement close to the interface was also analyzed by using SEM. ii Results of this study revealed, in L-condition, the μTBS of all cements were not significantly different. Only the μTBS of CS was not affected by the darkroom (D-condition). The μTBS of PV and RX were significantly decreasing in D-condition, approximately 36% and 88%, respectively. There were three pretest failure beams of RX-D. The main failure in this study was mixed failure, except for CS in both conditions which were cohesive failure within cement. In general, we found that adhesive failure was increasing in D-condition. For hardness and DC analysis results, CSL showed significantly higher values than PVL and RXL. in all testing times. Overall, the means of hardness and DC values of each cement were not significantly different when comparing 3 and 72 h. Except for the hardness of CS at 72 h, was significantly higher than 3 h. Within 2-15 μm distance from the resindentin interface, the DC analyses revealed CSL showed a strong positive correlation in both 3 and 72 h, contrast to those of RXL which showed the negative correlation. No correlation was found for PVL. For correlation of resin filler distribution and the distance from the resin-dentin interface, CSL showed a positive correlation, while RXL showed negative. No correlation was found for PVL. From the results of this study, it might be concluded that the μTBS of “Touch and cure” type dual-cured resin cement is not affected by the dark condition, while the conventional type does, and showed the higher both microhardness and DC. It might estimate that the “Touch and cure” reaction of mixed cement might probably occur approximately within 15 μm from the resindentin interface.; (主査) 教授 佐野 英彦, 教授 井上 哲, 教授 吉田 靖弘; 歯学研究科（口腔医学専攻）
• DOI: 10.14943/doctoral.k13864; https://doi.org/10.14943/doctoral.k13864
• Persistent ID (NDL): info:ndljp/pid/11660434; https://dl.ndl.go.jp/pid/11660434
• Collection: 障害者向け資料
• Collection (Materials For Handicapped People:1): テキストデータ
• Collection (particular): 国立国会図書館デジタルコレクション > デジタル化資料 > 博士論文; https://dl.ndl.go.jp/collections/A00014
• Acquisition Basis: 博士論文（自動収集）
• Date Accepted (W3CDTF): 2021-04-07T03:01:57+09:00
• Date Created (W3CDTF): 2020-03
• Format (IMT): PDF
• Access Restrictions: 国立国会図書館内限定公開
• Service for the Digitized Contents Transmission Service: 図書館・個人送信対象外
• Availability of remote photoduplication service: 可
• Periodical Title (URI): http://dx.doi.org/10.14943/doctoral.k13864; http://hdl.handle.net/2115/80678
• Is Referenced By (URI): http://hdl.handle.net/2115/78514
• Data Provider (Database): 国立国会図書館 : 国立国会図書館デジタルコレクション; https://dl.ndl.go.jp

• Summary, etc.: Recently, the new and novel “Touch and cure” technology for dual-cured resin cement was developed and introduced. This new technology is claimed that ...