Background: β-Tricalcium phosphate (β-TCP) is a popular synthetic bone graft substitute with excellent osteoconductive properties and bioabsorbability. However, its osteoinductive properties are inferior to those of autologous or allogeneic bone. Trace elements such as strontium (Sr), silica (Si), and zinc (Zn) have been reported to promote osteogenesis in materials. In this study, we aimed to determine whether a Si/Zn-substituted Sr apatite coating of β-TCP could enhance osteoinductive properties. Methods: The apatite-coated β-TCP disks were prepared using nanoparticle suspensions of silicate-substituted Sr apatite (SrSiP) or silicate- and Zn-co-substituted Sr apatite (SrZnSiP). Bone marrow mesenchymal cells (BMSCs) from rat femur were cultured and subsequently seeded at a density of 1.0 × 106/cm2 onto apatite-coated and non-coated β-TCP disks. In vitro, the β-TCP disks were then placed in osteogenic medium, and lactate dehydrogenase (LDH) activity was measured from supernatants after culture for 2 days. Additionally, after culture for 14 days, the mRNA expression of genes encoding osteocalcin (OC), alkaline phosphatase (ALP), bone morphogenetic protein-2 (BMP-2), and vascular endothelial growth factor (VEGF) was evaluated by qRT-PCR. In vivo, the β-TCP disks were transplanted subcutaneously into rats that were sacrificed after 4 weeks. Then, the harvested disks were evaluated biochemically (ALP activity, OC content, mRNA expression of OC, ALP, BMP-2, and VEGF measured by qRT-PCR), radiologically, and histologically. Results: Significantly higher mRNA expression of almost all evaluated osteogenic and angiogenic genes was observed in the SrZnSiP and SrSiP groups than in the non-coated group, with no significant cytotoxicity elicited by the apatite coating in vitro. Moreover, in vivo, the SrZnSiP and SrSiP groups showed significantly higher osteogenic and angiogenic gene expression and higher ALP activity and OC content than the non-coated group (P < 0.05). Radiological and histopathological findings revealed abundant bone formation in the apatite-coated group. Conclusions: Our findings indicate that apatite coating of β-TCP improves osteoinductive properties without inducing significant cytotoxicity.
博士（医学）・甲第805号・令和3年12月21日
© 2021. The Author(s).
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/. The Creative Commons Public Domain Dedication waiver (http://creativecommons.org/publicdomain/zero/1.0/) applies to the data made available in this article, unless otherwise stated in a credit line to the data.
identifier:BMC musculoskeletal disorders Vol.22 No.1 Article No.673 (2021 Aug)
identifier:14712474
identifier:http://ginmu.naramed-u.ac.jp/dspace/handle/10564/3954
identifier:BMC musculoskeletal disorders, 22(1): Article No.673
Collection (particular)国立国会図書館デジタルコレクション > デジタル化資料 > 博士論文
Date Accepted (W3CDTF)2022-04-04T15:10:33+09:00
Data Provider (Database)国立国会図書館 : 国立国会図書館デジタルコレクション